CEM I - PORTLAND CEMENT (OPC) 42.5-R
| Chemical analysis | Results (%) | Limit values |
| Silicon Oxide, % SiO2 | 19,37 | |
| Aluminium Oxide, % Al2O3 | 4,68 | |
| Iron Oxide, % Fe2O3 | 3,35 | |
| Calcium Oxide, % CaO | 63,08 | |
| Magnesium Oxide, % MgO | 1,42 | |
| Sulphur Oxide, % SO3 | 2,71 | ≤ 4,0% |
| Sodium Oxide, % Na2O | 0,29 | |
| Potassium Oxide, % K2O | 0,63 | |
| CI | 0,0089 | ≤ 0,10% |
| Loss on Ignition % ( L.O.I) | 3,28 | ≤ 5,0% |
| Insoluble Residue % (I.R) | 0,33 | ≤ 5,0% |
| Free lime | 0,73 | |
| Physical analysis | Results | Limit values |
| Initial Setting Time (minutes) | 155 | ≥ 60 |
| Final Setting Time (minutes) | 250 | |
| Soundness/Expansion (mm) | 1,0 | ≤ 10 |
| Specific Surface Area Blaine (cm2/g) | 3275 | |
| 2 days - Compressive Strength (MPa) | 24,0 | ≥ 20 |
| 7 days - Compressive Strength (MPa) | 39,2 | |
| 28 days - Compressive Strength (MPa) | 52,6 | ≥ 42,5 ; ≤ 62,5 |
A hydraulic cement produced by milling Portland cement clinker (TS 3441) together with gypsum.
It is classified as PC 42.5, and PC 52.5. "PC" is the symbol for Portland cement while the numbers 42.5, 52.5 indicate the minimum desired strength value achieved within 28 days.
Produced in compliance with TS 19 (Turkish), EN 197-1 (British) and (American) standards.
The quality is also in compliance with Russian standards and the factory has the certificate enabling us to export to Russia.
It is generally used in works requiring high strength values, concrete works performed at low temperatures, precast buildings, tunnel-form applications, building chemical maunfacturing and foundations.
- General purpose
- All kinds of concrete structures
- High Buildings
- Road pavements
- Sidewalk Concretes
- Ground concretes
- Buildings made up with slide-molds
- General purpose prefabricated concrete components
- Bridges
- Railway Slippers
- Art Works (viaducts, sub-passageways, upper passageways)
- Water Storages
- Concrete Pipes
- Concrete Brickets
- Tunnel Mould Applications
- Pretensioning Concretes
|